WIM PLATTE VARIO-BUILDING BOARD

Maximum freedom in space arrangement.

It is designed to be used for wall and floor cladding both indoors and outdoors, especially in areas exposed to water and moisture. It is extremely easy to work with, which makes it possible to create any shapes (including semi-circular forms) in a simple way. This is a modern product – lightweight, multifunctional, clean, easy to transport, and simple and quick to process. At the same time, it is extremely durable, with high resistance to loads and stiffness of the constructed structure. It is resistant to water and provides good thermal and acoustic insulation.

PROPERTIES:

•  leveling wall surfaces,
•  encasing bathtubs, shower trays, concealed installation systems,
•  covering water and sewage pipes and risers,
• as a material for constructing countertops for sinks, shelves, steps, seating, for example, in SPA&Wellness bathrooms,
•  drywall construction – completely replaces plaster in the bathroom,
•  use in areas exposed to intensive moisture and condensation such as bathrooms, shower cabins, steam rooms,
• an ideal base for ceramic tiles, mosaics, textured plasters or paint coatings,
• excellent thermal insulation,
• excellent acoustic insulation,
• completely waterproof,
• freedom in interior design,
• very lightweight

More information:

Composition: a core made of extruded polystyrene foam (XPS), in compliance with PN-EN 13164:2010 standard, reinforced on both sides with a fiberglass mesh and covered with a special high-quality cement mortar enriched with modified synthetic resins.

Declared thermal conductivity coefficient – λD λ design value in accordance with Z-23.15-1476: DIN 4108-1, 0.03

d = 6 mm: 0.029

d = 12 mm: 0.029 d = 20 mm: 0.029

d = 30 mm: 0.029 d = 50 mm: 0.029

Apparent density of the core: ≥ 30 kg/m³

Compressive strength at 10% relative deformation: ≥ 0.3 MPa

Water absorption:

• after 1 hour: ≤ 1 kg/m²
• after 24 hours: ≤ 1 kg/m²

Tensile strength perpendicular to the frontal surfaces:

• after 28 days in laboratory conditions: ≥ 0.4 MPa
• after 7 days in laboratory conditions and 21 days in water: ≥ 0.4 MPa
• after 7 days in laboratory conditions and 14 days at a temperature of +70°C: ≥ 0.4 MPa
• after 7 days in laboratory conditions and 21 days in water, followed by 25 cycles of freezing and thawing in water: ≥ 0.14 MPa

Temperature range of use: -50°C / +75°C

Reaction to fire class: E

Product capability: